Keep The Cooling And Lubrication of The Crate Mould Clean from xiu's blog

advertisement

In the process of plastic melting and plasticizing, the Crate Mould(FURNITUREMOULD) is prone to defects. The solution is to reduce the quenching stress after heat treatment to a minimum, because the quenching stress and the mesh carbonized structure, under the action of grinding force, can easily crack the workpiece due to phase transformation of the structure. Reasonable use of cooling and lubricating fluid, play the three major roles of cooling, washing and lubrication, keep the cooling and lubricating clean, thus control the grinding heat within the allowable range, and prevent the thermal deformation of the workpiece.

Specific Operation of Processing Defects of Crate Mould:

1. Improve the cooling conditions during grinding, such as adopting oil impregnated grinding wheel or internal cooling grinding wheel and other measures. When cutting fluid is introduced into the center of grinding wheel, cutting fluid can directly enter grinding area to play an effective cooling role and prevent workpiece surface burns. Reasonable use of cooling and lubricating fluid, play the three major roles of cooling, washing and lubrication, keep the cooling and lubricating clean, thus control the grinding heat within the allowable range, and prevent the thermal deformation of the workpiece.

2. Reduce the quenching stress after heat treatment to the minimum, because under the action of grinding force, the quenching stress and reticular carbonized structure can easily cause cracks in the workpiece due to phase transformation of the structure. In order to eliminate the grinding residual stress of high precision dies, low temperature aging treatment should be carried out after grinding to improve toughness.

3. To eliminate grinding stress, the crate mould can also be immersed in salt bath at 260 ~ 315℃ for 1.5min, and then cooled in oil at 30℃, thus the hardness can be reduced by 1HRC and the residual stress can be reduced by 40% ~ 65%.

4. For precision grinding of precision dies with dimensional tolerance within 0.01mm, attention should be paid to the influence of ambient temperature and constant temperature grinding is required. From the calculation, it can be seen that when the temperature difference of 300mm long steel parts is 3℃, the material has a change of about 10.8μm (10.8=1.2×3×3, the deformation amount per 100mm is 1.2μm/℃). All finishing processes should fully consider the influence of this factor.

5. Electrolytic grinding is adopted to improve the manufacturing precision and surface quality of the crate mould. During electrolytic grinding, the grinding wheel scrapes off oxide film instead of metal, so the grinding force is small, the grinding heat is also small, no grinding burr, crack, burn and other phenomena will occur, and the general surface roughness can be better than Ra0.16μm; In addition, the abrasion of the grinding wheel is reduced. For example, when grinding hard alloy, the abrasion of the silicon carbide grinding wheel is about 400% ~ 600% of the weight of the hard alloy, while when electrolytic grinding is used, the abrasion of the grinding wheel is only 50% ~ 100% of the abrasion of the hard alloy.

If you are interested in our products, you can click Household Product Mould to learn more information.


Share:
Previous post     
     Next post
     Blog home

The Wall

No comments
You need to sign in to comment
advertisement